SUS301(sus301和sus304区别)

sus301/302/303/304的元素组成及含量是怎样的

部分不锈钢化学成份表

规格 化学成份(%)

中国C Si Mn P S Ni Cr Mo

0Cr19Ni9 ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.035 8.00-10.50 18.00-20.00

0Cr19Ni11 ≤0.030 ≤1.00 ≤2.00 ≤0.035 ≤0.035 9.00-13.00 18.00-20.00

0Cr17Ni12Mo2 ≤0.08 ≤1.00 ≤2.00 ≤0.035 ≤0.035 10.00-14.00 16.00-18.00 2.00-3.00

0Cr19Ni14Mo2 ≤0.030 ≤1.00 ≤2.00 ≤0.035 ≤0.035 12.00-15.00 16.00-18.00 2.00-3.00

日本 SUS304 ≤0.08 ≤1.00 ≤2.00 ≤0.040 ≤0.040 8.00-11.00 18.00-20.00

SUS304L ≤0.030 ≤1.00 ≤2.00 ≤0.040 ≤0.040 9.00-13.00 18.00-20.00

SUS316 ≤0.08 ≤1.00 ≤2.00 ≤0.040 ≤0.040 10.00-14.00 16.00-18.00 2.00-3.00

SUS316L ≤0.030 ≤1.00 ≤2.00 ≤0.040 ≤0.040 12.00-16.00 16.00-18.00 2.00-3.00

美国 Tp304 ≤0.08 ≤0.75 ≤2.00 ≤0.040 ≤0.040 8.00-11.00 18.00-20.00

Tp304L ≤0.035 ≤0.75 ≤2.00 ≤0.040 ≤0.040 8.00-13.00 18.00-20.00

Tp316 ≤0.08 ≤0.75 ≤2.00 ≤0.040 ≤0.040 11.00-14.00 16.00-18.00 2.00-3.00

Tp316L ≤0.035 ≤0.75 ≤2.00 ≤0.040 ≤0.040 10.00-15.00 16.00-18.00 2.00-3.00不建议使用一般不锈钢做弹性片，你所列的都是3系不锈钢，作为弹片使用的不锈钢首先在牌号标示上面就有所不同，比如301弹性不锈钢： sus301-csp-1/2h 表示是后处理不一样的3系弹性不锈钢材料，重点在于后面的处理 1/2h,h，等等，所代表的拉伸强度，弯曲强度等物理性能不一样，需查看具体标准参数，来进行对比，首先明白概念了，后面的对比都简单

sus301和sus 304有什么区别?

SUS301(不銹钢)：Cr (铬) 成分比 SUS304 低，耐蚀性较差，但冷间加工能得到非常高度的拉加及硬度，其特性用途广大，因弹性佳，故目前在Notebook常被广泛运用在防EMI上，做弹性接触部份，但常用厚度在 0.4T ~ 0.07T 之间。运用上必须指定级数,以期达到设计之需求(例如弹力,强度).并须注意301材料有金属结晶性方向性,越**数者越是硬且脆,若成型上不注意,易造成隅角及侧壁裂纹.

SUS 301 : 适合用弹性用途,含碳量高,硬度高,不易弹性疲乏.延展性不好,不易抽伸. SUS 304 : 不适合用弹性用途,含碳量低硬度低(软). SUS 430 : 材料含杂质较多(不纯),导致硬度不稳定.

1.若两著硬度接近 如(SUS301 3/4H跟SUS304 H)虽然硬度相同,但是用在弹性的产品上 SUS 304 H 较易产生弹性疲乏.

2.材料厚度影响硬度公差(越厚公差越大).

SUS 301：表面较雾,磁性比430弱,耐蚀性强,弹性很好,不易疲泛,适合於冷加工,有硬度要求,硬度与弹性成正比，用于弹片及强度要求高之支架,面板等

SUS 304：无磁性,耐蚀性较强,弹性好,材料无明显丝向,冷加工效果好,耐深抽,有硬度区别,此材料分2B面与AB面,即雾面与镜面之分，用于支架,连结器和餐具等csp是指加工方法：连铸连轧

sus301 csp-h与sus301-h之间区别是sus301-h没有指定加工方法。

hj指硬度：

sus301-csp-1/4h、sus301-1/4h 硬度大于hv250

sus301-csp-1/2h、sus301-1/2h 硬度大于 hv310

sus301-csp-3/4h、sus301-3/4h 硬度大于 hv370

sus301-csp-h、sus301-h 硬度大于 hv430